A bone replaceable artificial bone substitute: morphological and physiochemical characterizations.

J. C. Park, D. W. Han, H. Suh

Research output: Contribution to journalArticle

10 Citations (Scopus)

Abstract

A composite material consisting of carbonate apatite (CAp) and type I atelocollagen (AtCol) (88/12 in wt/wt%) was designed for use as an artificial bone substitute. CAp was synthesized at 58 degrees C by a solution-precipitation method and then heated at either 980 degrees C or 1,200 degrees C. In this study, type I AtCol was purified from bovine tail skins. A CAp-AtCol mixture was prepared by centirfugation and condensed into composite rods or disks. The scanning electron-microscopic (SEM) characterization indicated that the CAp synthesized at 58 degrees C displayed a crystallinity similar to that of natural bone and had a high porosity (mean pore size: about 3-10 microns in diameter). SEM also revealed that the CAp heated at 980 degrees C was more porous than that sintered at 1,200 degrees C, and the 1,200 degrees C-heated particles were more uniformly encapsulated by the AtCol fibers than the 980 degrees C-heated ones. A Fourier transformed-infrared spectroscopic analysis showed that the bands characteristic of carbonate ions were clearly observed in the 58 degrees C-synthesized CAp. To enhance the intramolecular cross-linking between the collagen molecules, CAp-AtCol composites were irradiated by ultraviolet (UV) ray (wave length 254 nm) for 4 hours or vacuum-dried at 150 degrees C for 2 hours. Compared to the non cross-linked composites, the UV-irradiated or dehydrothermally cross-linked composites showed significantly (p < 0.05) low collagen degradation and swelling ratio. Preliminary mechanical data demonstrated that the compressive strengths of the CAp-AtCol composites were higher than the values reported for bone.

Original languageEnglish
Pages (from-to)468-476
Number of pages9
JournalYonsei medical journal
Volume41
Issue number4
DOIs
Publication statusPublished - 2000 Aug

Fingerprint

Bone Substitutes
Bone and Bones
Collagen
Electrons
Compressive Strength
carboapatite
Porosity
Carbonates
Ultraviolet Rays
Vacuum
atelocollagen
Ions
Skin

All Science Journal Classification (ASJC) codes

  • Medicine(all)

Cite this

@article{67f9c98c5ca340ae9b5bab8bd5cf7631,
title = "A bone replaceable artificial bone substitute: morphological and physiochemical characterizations.",
abstract = "A composite material consisting of carbonate apatite (CAp) and type I atelocollagen (AtCol) (88/12 in wt/wt{\%}) was designed for use as an artificial bone substitute. CAp was synthesized at 58 degrees C by a solution-precipitation method and then heated at either 980 degrees C or 1,200 degrees C. In this study, type I AtCol was purified from bovine tail skins. A CAp-AtCol mixture was prepared by centirfugation and condensed into composite rods or disks. The scanning electron-microscopic (SEM) characterization indicated that the CAp synthesized at 58 degrees C displayed a crystallinity similar to that of natural bone and had a high porosity (mean pore size: about 3-10 microns in diameter). SEM also revealed that the CAp heated at 980 degrees C was more porous than that sintered at 1,200 degrees C, and the 1,200 degrees C-heated particles were more uniformly encapsulated by the AtCol fibers than the 980 degrees C-heated ones. A Fourier transformed-infrared spectroscopic analysis showed that the bands characteristic of carbonate ions were clearly observed in the 58 degrees C-synthesized CAp. To enhance the intramolecular cross-linking between the collagen molecules, CAp-AtCol composites were irradiated by ultraviolet (UV) ray (wave length 254 nm) for 4 hours or vacuum-dried at 150 degrees C for 2 hours. Compared to the non cross-linked composites, the UV-irradiated or dehydrothermally cross-linked composites showed significantly (p < 0.05) low collagen degradation and swelling ratio. Preliminary mechanical data demonstrated that the compressive strengths of the CAp-AtCol composites were higher than the values reported for bone.",
author = "Park, {J. C.} and Han, {D. W.} and H. Suh",
year = "2000",
month = "8",
doi = "10.3349/ymj.2000.41.4.468",
language = "English",
volume = "41",
pages = "468--476",
journal = "Yonsei Medical Journal",
issn = "0513-5796",
publisher = "Yonsei University College of Medicine",
number = "4",

}

A bone replaceable artificial bone substitute : morphological and physiochemical characterizations. / Park, J. C.; Han, D. W.; Suh, H.

In: Yonsei medical journal, Vol. 41, No. 4, 08.2000, p. 468-476.

Research output: Contribution to journalArticle

TY - JOUR

T1 - A bone replaceable artificial bone substitute

T2 - morphological and physiochemical characterizations.

AU - Park, J. C.

AU - Han, D. W.

AU - Suh, H.

PY - 2000/8

Y1 - 2000/8

N2 - A composite material consisting of carbonate apatite (CAp) and type I atelocollagen (AtCol) (88/12 in wt/wt%) was designed for use as an artificial bone substitute. CAp was synthesized at 58 degrees C by a solution-precipitation method and then heated at either 980 degrees C or 1,200 degrees C. In this study, type I AtCol was purified from bovine tail skins. A CAp-AtCol mixture was prepared by centirfugation and condensed into composite rods or disks. The scanning electron-microscopic (SEM) characterization indicated that the CAp synthesized at 58 degrees C displayed a crystallinity similar to that of natural bone and had a high porosity (mean pore size: about 3-10 microns in diameter). SEM also revealed that the CAp heated at 980 degrees C was more porous than that sintered at 1,200 degrees C, and the 1,200 degrees C-heated particles were more uniformly encapsulated by the AtCol fibers than the 980 degrees C-heated ones. A Fourier transformed-infrared spectroscopic analysis showed that the bands characteristic of carbonate ions were clearly observed in the 58 degrees C-synthesized CAp. To enhance the intramolecular cross-linking between the collagen molecules, CAp-AtCol composites were irradiated by ultraviolet (UV) ray (wave length 254 nm) for 4 hours or vacuum-dried at 150 degrees C for 2 hours. Compared to the non cross-linked composites, the UV-irradiated or dehydrothermally cross-linked composites showed significantly (p < 0.05) low collagen degradation and swelling ratio. Preliminary mechanical data demonstrated that the compressive strengths of the CAp-AtCol composites were higher than the values reported for bone.

AB - A composite material consisting of carbonate apatite (CAp) and type I atelocollagen (AtCol) (88/12 in wt/wt%) was designed for use as an artificial bone substitute. CAp was synthesized at 58 degrees C by a solution-precipitation method and then heated at either 980 degrees C or 1,200 degrees C. In this study, type I AtCol was purified from bovine tail skins. A CAp-AtCol mixture was prepared by centirfugation and condensed into composite rods or disks. The scanning electron-microscopic (SEM) characterization indicated that the CAp synthesized at 58 degrees C displayed a crystallinity similar to that of natural bone and had a high porosity (mean pore size: about 3-10 microns in diameter). SEM also revealed that the CAp heated at 980 degrees C was more porous than that sintered at 1,200 degrees C, and the 1,200 degrees C-heated particles were more uniformly encapsulated by the AtCol fibers than the 980 degrees C-heated ones. A Fourier transformed-infrared spectroscopic analysis showed that the bands characteristic of carbonate ions were clearly observed in the 58 degrees C-synthesized CAp. To enhance the intramolecular cross-linking between the collagen molecules, CAp-AtCol composites were irradiated by ultraviolet (UV) ray (wave length 254 nm) for 4 hours or vacuum-dried at 150 degrees C for 2 hours. Compared to the non cross-linked composites, the UV-irradiated or dehydrothermally cross-linked composites showed significantly (p < 0.05) low collagen degradation and swelling ratio. Preliminary mechanical data demonstrated that the compressive strengths of the CAp-AtCol composites were higher than the values reported for bone.

UR - http://www.scopus.com/inward/record.url?scp=0034243581&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0034243581&partnerID=8YFLogxK

U2 - 10.3349/ymj.2000.41.4.468

DO - 10.3349/ymj.2000.41.4.468

M3 - Article

C2 - 10992808

AN - SCOPUS:0034243581

VL - 41

SP - 468

EP - 476

JO - Yonsei Medical Journal

JF - Yonsei Medical Journal

SN - 0513-5796

IS - 4

ER -