Combined Effects of Ultrasonic Melt Treatment and Cu/Mg Solute on the Microstructure and Mechanical Properties of a Hypoeutectic Al-7Si Alloy

Soo Bae Kim, Young Hee Cho, Jung Moo Lee, Jae Gil Jung, Young-Kook Lee

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

The effect of Cu/Mg solute combined with ultrasonic melt treatment (UST) on the microstructure and mechanical properties of a hypoeutectic Al-7Si alloy was investigated. Cu up to 4 wt pct and Mg to 1 wt pct were added to the alloy and UST was performed at about 100 °C above the liquidus temperature. UST at such a high temperature was ineffective in refining grain sizes but enhanced the microstructural homogeneity of the alloys with the refinement of α-Al secondary dendrite arm spacing (SDAS). It was found that both the grain size and the SDAS were solute sensitive: In the Al-7Si alloy with UST they insignificantly changed with Cu but decreased with an increase in Mg content. Along with the structural refinement, UST was likely to affect the solute redistribution and the subsequent formation of secondary phases (e.g., eutectic Si and Cu/Mg-rich intermetallic compounds (IMCs)). Quantitative analysis indicated that UST had significantly minimized microsegregation of Cu and Mg solutes, decreasing the amount of the IMCs finely and uniformly distributed. The underlying reason was attributed to the reduction in the size of the SDAS, which enabled the solid-state diffusion to occur more efficiently upon solidification. The most significant increase in the tensile properties was achieved for the Al-7Si-2Cu-1Mg alloy with UST where the SDAS was well refined and the grain size was the smallest among the alloys investigated. The important role of UST on the casting structure refinement and the solute distribution is discussed and the resulting mechanical properties are further explored.

Original languageEnglish
Pages (from-to)1534-1544
Number of pages11
JournalMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
Volume50
Issue number3
DOIs
Publication statusPublished - 2019 Mar 15

Fingerprint

solutes
ultrasonics
Ultrasonics
mechanical properties
Mechanical properties
microstructure
Microstructure
dendrites
spacing
Dendrites (metallography)
grain size
Intermetallics
intermetallics
tensile properties
liquidus
refining
Tensile properties
eutectics
Eutectics
quantitative analysis

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys

Cite this

@article{9d042ce0b10d43cf98c7208506780741,
title = "Combined Effects of Ultrasonic Melt Treatment and Cu/Mg Solute on the Microstructure and Mechanical Properties of a Hypoeutectic Al-7Si Alloy",
abstract = "The effect of Cu/Mg solute combined with ultrasonic melt treatment (UST) on the microstructure and mechanical properties of a hypoeutectic Al-7Si alloy was investigated. Cu up to 4 wt pct and Mg to 1 wt pct were added to the alloy and UST was performed at about 100 °C above the liquidus temperature. UST at such a high temperature was ineffective in refining grain sizes but enhanced the microstructural homogeneity of the alloys with the refinement of α-Al secondary dendrite arm spacing (SDAS). It was found that both the grain size and the SDAS were solute sensitive: In the Al-7Si alloy with UST they insignificantly changed with Cu but decreased with an increase in Mg content. Along with the structural refinement, UST was likely to affect the solute redistribution and the subsequent formation of secondary phases (e.g., eutectic Si and Cu/Mg-rich intermetallic compounds (IMCs)). Quantitative analysis indicated that UST had significantly minimized microsegregation of Cu and Mg solutes, decreasing the amount of the IMCs finely and uniformly distributed. The underlying reason was attributed to the reduction in the size of the SDAS, which enabled the solid-state diffusion to occur more efficiently upon solidification. The most significant increase in the tensile properties was achieved for the Al-7Si-2Cu-1Mg alloy with UST where the SDAS was well refined and the grain size was the smallest among the alloys investigated. The important role of UST on the casting structure refinement and the solute distribution is discussed and the resulting mechanical properties are further explored.",
author = "Kim, {Soo Bae} and Cho, {Young Hee} and Lee, {Jung Moo} and Jung, {Jae Gil} and Young-Kook Lee",
year = "2019",
month = "3",
day = "15",
doi = "10.1007/s11661-018-5069-2",
language = "English",
volume = "50",
pages = "1534--1544",
journal = "Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science",
issn = "1073-5623",
publisher = "Springer Boston",
number = "3",

}

TY - JOUR

T1 - Combined Effects of Ultrasonic Melt Treatment and Cu/Mg Solute on the Microstructure and Mechanical Properties of a Hypoeutectic Al-7Si Alloy

AU - Kim, Soo Bae

AU - Cho, Young Hee

AU - Lee, Jung Moo

AU - Jung, Jae Gil

AU - Lee, Young-Kook

PY - 2019/3/15

Y1 - 2019/3/15

N2 - The effect of Cu/Mg solute combined with ultrasonic melt treatment (UST) on the microstructure and mechanical properties of a hypoeutectic Al-7Si alloy was investigated. Cu up to 4 wt pct and Mg to 1 wt pct were added to the alloy and UST was performed at about 100 °C above the liquidus temperature. UST at such a high temperature was ineffective in refining grain sizes but enhanced the microstructural homogeneity of the alloys with the refinement of α-Al secondary dendrite arm spacing (SDAS). It was found that both the grain size and the SDAS were solute sensitive: In the Al-7Si alloy with UST they insignificantly changed with Cu but decreased with an increase in Mg content. Along with the structural refinement, UST was likely to affect the solute redistribution and the subsequent formation of secondary phases (e.g., eutectic Si and Cu/Mg-rich intermetallic compounds (IMCs)). Quantitative analysis indicated that UST had significantly minimized microsegregation of Cu and Mg solutes, decreasing the amount of the IMCs finely and uniformly distributed. The underlying reason was attributed to the reduction in the size of the SDAS, which enabled the solid-state diffusion to occur more efficiently upon solidification. The most significant increase in the tensile properties was achieved for the Al-7Si-2Cu-1Mg alloy with UST where the SDAS was well refined and the grain size was the smallest among the alloys investigated. The important role of UST on the casting structure refinement and the solute distribution is discussed and the resulting mechanical properties are further explored.

AB - The effect of Cu/Mg solute combined with ultrasonic melt treatment (UST) on the microstructure and mechanical properties of a hypoeutectic Al-7Si alloy was investigated. Cu up to 4 wt pct and Mg to 1 wt pct were added to the alloy and UST was performed at about 100 °C above the liquidus temperature. UST at such a high temperature was ineffective in refining grain sizes but enhanced the microstructural homogeneity of the alloys with the refinement of α-Al secondary dendrite arm spacing (SDAS). It was found that both the grain size and the SDAS were solute sensitive: In the Al-7Si alloy with UST they insignificantly changed with Cu but decreased with an increase in Mg content. Along with the structural refinement, UST was likely to affect the solute redistribution and the subsequent formation of secondary phases (e.g., eutectic Si and Cu/Mg-rich intermetallic compounds (IMCs)). Quantitative analysis indicated that UST had significantly minimized microsegregation of Cu and Mg solutes, decreasing the amount of the IMCs finely and uniformly distributed. The underlying reason was attributed to the reduction in the size of the SDAS, which enabled the solid-state diffusion to occur more efficiently upon solidification. The most significant increase in the tensile properties was achieved for the Al-7Si-2Cu-1Mg alloy with UST where the SDAS was well refined and the grain size was the smallest among the alloys investigated. The important role of UST on the casting structure refinement and the solute distribution is discussed and the resulting mechanical properties are further explored.

UR - http://www.scopus.com/inward/record.url?scp=85058861923&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85058861923&partnerID=8YFLogxK

U2 - 10.1007/s11661-018-5069-2

DO - 10.1007/s11661-018-5069-2

M3 - Article

AN - SCOPUS:85058861923

VL - 50

SP - 1534

EP - 1544

JO - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

JF - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

SN - 1073-5623

IS - 3

ER -