A thermoelectric coated grain nanocomposite CuInTe2/SnTe with eco-friendly elements was synthesized. The nanocomposite contains a coating layer of CuInTe2and SnO2at the grain boundaries of the SnTe matrix. The coating layer was synthesized using the cation exchange process considering the hard soft acid base (HSAB) concept, the solubility product, and crystal structure. The CuInTe2coating layer blocks the low energy carriers of the composite resulting in 40% enhancement of the Seebeck coefficient due to energy filtering. The coherent phonon scattering by the coating layer of CuInTe2effectively reduces the lattice thermal conductivity to almost the minimum theoretical limit. The thermoelectric figure of merit (zT) for the CuInTe2/SnTe nanocomposite was as high as 1.68 at 823 K, which is significantly higher than that of bulk SnTe in the mid-temperature range. The averagezTfrom 373 K to 823 K for the nanocomposite was 0.76, which is promising for utilization in industrial application.
|Number of pages||8|
|Journal||Journal of Materials Chemistry A|
|Publication status||Published - 2021 Jul 14|
Bibliographical noteFunding Information:
This work was supported by the National Research Foundation of Korea (NRF) grant funded by the Korea government (MSIT) (NRF-2018R1A2B2005455). This work was supported by the Korea Basic Science Institute (National Research Facilities and Equipment Center) grant funded by the Ministry of Education (2020R 1A 6C 101B194).
© The Royal Society of Chemistry 2021.
All Science Journal Classification (ASJC) codes
- Renewable Energy, Sustainability and the Environment
- Materials Science(all)