The understanding and tailoring of the electrochemistry of graphite is of significant industrial importance. We develop a method of etching pits into the basal planes of highly oriented pyrolytic graphite (HOPG) by electrolysis. The etching of HOPG was realized by performing electrochemical reactions at alternating potentials at room temperature, and the resulting membranes are characterized using atomic force microscopy, scanning electron microscopy, X-ray photoelectron spectra, X-ray diffraction, Raman spectroscopy, Fourier transform infrared spectrscopy, and cyclic voltammetry. Etching only occurs when the electrolysis at negative bias is followed by a brief switch to a positive bias. The size of the etched pits can be tuned by varying the applied potential and reaction time, with deeper pits formed with increased redox cycles and reaction time. Cyclic voltammetry reveals that the electrochemical performance is enhanced greatly as etching progresses due to exposure of edge sites. For its ease of application, efficiency and low cost, our wet etching approach has great promise as a method to develop high active electrodes and nanoporous membranes at large scales for various industrial applications.
Bibliographical noteFunding Information:
We gratefully acknowledge funding from a competitive research programme under the auspices of the Singapore government's National Research Foundation (No. NRF-CRP9-2011-04). H. A. acknowledges the support from the National Natural Science Foundation of China (NSFC-31571029) and the National Key R&D Program of China (2016YFD0400800). B.H.T. acknowledges financial support from the Agency for Science, Technology and Research in Singapore. J. G. S. M. is supported by the National Research Foundation Singapore under its National Research Foundation (NRF) Environmental and Water Technologies (EWT) PhD Scholarship Programme and administered by the Environment and Water Industry Programme Office (EWI). M.P. acknowledges a Tier 2 grant (MOE2013-T2-1-056; ARC 35/13) from the Ministry of Education - Singapore.
© 2017 Elsevier Ltd
All Science Journal Classification (ASJC) codes
- Materials Science(all)