TY - JOUR
T1 - Influence of MgO and Al2O3 contents on viscosity of blast furnace type slags containing FeO
AU - Kim, Joo Ro
AU - Lee, Young Seok
AU - Min, Dong Joon
AU - Jung, Sung Mo
AU - Yi, Sang Ho
N1 - Copyright:
Copyright 2017 Elsevier B.V., All rights reserved.
PY - 2004
Y1 - 2004
N2 - The viscosities of CaO-SiO2-Al2O3-MgO-FeO slag were measured under conditions of C/S=1.35-1.45, 10-18 mass% Al 2O3, 3.5-10 mass% MgO and 5 mass% FeO. The bosh slag with 10 mass% Al2O3 content had the lowest melting temperature and the widest solid-liquid coexisting region at about 5 mass% MgO, while in case of 14 mass% Al2O3, an increase in a MgO content from about 3.5 to 10 mass% raised the melting point of bosh slag. The viscosity of bosh slag also exhibited a minimum value at about 7 mass% MgO at temperatures above 1 723 K. However, it was not significantly changed with varying MgO content. On the hand, with increasing Al2O3 content, the viscosity of bosh slag increased at a fixed C/S and MgO content. Based on the melting temperature and the behavior of viscosity at a fixed temperature, it could be proposed that the MgO and Al2O3 contents in bosh slag should be maintained around 5 and 10 mass%, respectively, for high pulverized-coal ratio (PCR) and low slag volume operations in blast furnace.
AB - The viscosities of CaO-SiO2-Al2O3-MgO-FeO slag were measured under conditions of C/S=1.35-1.45, 10-18 mass% Al 2O3, 3.5-10 mass% MgO and 5 mass% FeO. The bosh slag with 10 mass% Al2O3 content had the lowest melting temperature and the widest solid-liquid coexisting region at about 5 mass% MgO, while in case of 14 mass% Al2O3, an increase in a MgO content from about 3.5 to 10 mass% raised the melting point of bosh slag. The viscosity of bosh slag also exhibited a minimum value at about 7 mass% MgO at temperatures above 1 723 K. However, it was not significantly changed with varying MgO content. On the hand, with increasing Al2O3 content, the viscosity of bosh slag increased at a fixed C/S and MgO content. Based on the melting temperature and the behavior of viscosity at a fixed temperature, it could be proposed that the MgO and Al2O3 contents in bosh slag should be maintained around 5 and 10 mass%, respectively, for high pulverized-coal ratio (PCR) and low slag volume operations in blast furnace.
UR - http://www.scopus.com/inward/record.url?scp=6344291684&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=6344291684&partnerID=8YFLogxK
U2 - 10.2355/isijinternational.44.1291
DO - 10.2355/isijinternational.44.1291
M3 - Article
AN - SCOPUS:6344291684
VL - 44
SP - 1291
EP - 1297
JO - Transactions of the Iron and Steel Institute of Japan
JF - Transactions of the Iron and Steel Institute of Japan
SN - 0915-1559
IS - 8
ER -