Influence of TiO 2 on the viscous behavior of calcium silicate melts containing 17 mass% Al 2O 3 and 10 mass% MgO

Il Sohn, Wanlin Wang, Hiroyuki Matsuura, Fumitaka Tsukihashi, Dong Joon Min

Research output: Contribution to journalArticle

55 Citations (Scopus)

Abstract

A study was conducted to investigate the Influence of TiO 3 on the Viscous behavior of calcium silicate melts containing 17 mass% Al 2O 3 and 10 mass% MgO. Samples were synthesized using reagent grade chemicals of CaO, SiO 2, MgO, Al 2O 3, and TiO 2. The samples were premelted at 1 773 K under 0.4 L/min of Ar in a Pt crucible to obtain a homogeneous slag sample. Post-experimental chemical composition using X-Ray Fluorescence (XRF) spectroscopy showed no apparent change. The viscosity of 120 g of slag placed in a Pt crucible was measured using a rotating spindle connected to a calibrated Brookfield digital rheometer. Effect of TiO 2 at constant temperature of 1 773 K at various CaO/SiO 2 ratio was provided. The temperature dependence of the viscosity at CaO/SiO 2 of 0.8 and various TiO 2 content was shown where the viscosity decreased with increasing temperatures.

Original languageEnglish
Pages (from-to)158-160
Number of pages3
JournalISIJ International
Volume52
Issue number1
DOIs
Publication statusPublished - 2012 Jan 23

Fingerprint

Calcium silicate
Crucibles
Viscosity
Slags
Rheometers
Temperature
Chemical analysis
calcium silicate

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Cite this

Sohn, Il ; Wang, Wanlin ; Matsuura, Hiroyuki ; Tsukihashi, Fumitaka ; Min, Dong Joon. / Influence of TiO 2 on the viscous behavior of calcium silicate melts containing 17 mass% Al 2O 3 and 10 mass% MgO. In: ISIJ International. 2012 ; Vol. 52, No. 1. pp. 158-160.
@article{3b39df304389492c895cb7dcc080547b,
title = "Influence of TiO 2 on the viscous behavior of calcium silicate melts containing 17 mass{\%} Al 2O 3 and 10 mass{\%} MgO",
abstract = "A study was conducted to investigate the Influence of TiO 3 on the Viscous behavior of calcium silicate melts containing 17 mass{\%} Al 2O 3 and 10 mass{\%} MgO. Samples were synthesized using reagent grade chemicals of CaO, SiO 2, MgO, Al 2O 3, and TiO 2. The samples were premelted at 1 773 K under 0.4 L/min of Ar in a Pt crucible to obtain a homogeneous slag sample. Post-experimental chemical composition using X-Ray Fluorescence (XRF) spectroscopy showed no apparent change. The viscosity of 120 g of slag placed in a Pt crucible was measured using a rotating spindle connected to a calibrated Brookfield digital rheometer. Effect of TiO 2 at constant temperature of 1 773 K at various CaO/SiO 2 ratio was provided. The temperature dependence of the viscosity at CaO/SiO 2 of 0.8 and various TiO 2 content was shown where the viscosity decreased with increasing temperatures.",
author = "Il Sohn and Wanlin Wang and Hiroyuki Matsuura and Fumitaka Tsukihashi and Min, {Dong Joon}",
year = "2012",
month = "1",
day = "23",
doi = "10.2355/isijinternational.52.158",
language = "English",
volume = "52",
pages = "158--160",
journal = "ISIJ International",
issn = "0915-1559",
publisher = "Iron and Steel Institute of Japan",
number = "1",

}

Influence of TiO 2 on the viscous behavior of calcium silicate melts containing 17 mass% Al 2O 3 and 10 mass% MgO. / Sohn, Il; Wang, Wanlin; Matsuura, Hiroyuki; Tsukihashi, Fumitaka; Min, Dong Joon.

In: ISIJ International, Vol. 52, No. 1, 23.01.2012, p. 158-160.

Research output: Contribution to journalArticle

TY - JOUR

T1 - Influence of TiO 2 on the viscous behavior of calcium silicate melts containing 17 mass% Al 2O 3 and 10 mass% MgO

AU - Sohn, Il

AU - Wang, Wanlin

AU - Matsuura, Hiroyuki

AU - Tsukihashi, Fumitaka

AU - Min, Dong Joon

PY - 2012/1/23

Y1 - 2012/1/23

N2 - A study was conducted to investigate the Influence of TiO 3 on the Viscous behavior of calcium silicate melts containing 17 mass% Al 2O 3 and 10 mass% MgO. Samples were synthesized using reagent grade chemicals of CaO, SiO 2, MgO, Al 2O 3, and TiO 2. The samples were premelted at 1 773 K under 0.4 L/min of Ar in a Pt crucible to obtain a homogeneous slag sample. Post-experimental chemical composition using X-Ray Fluorescence (XRF) spectroscopy showed no apparent change. The viscosity of 120 g of slag placed in a Pt crucible was measured using a rotating spindle connected to a calibrated Brookfield digital rheometer. Effect of TiO 2 at constant temperature of 1 773 K at various CaO/SiO 2 ratio was provided. The temperature dependence of the viscosity at CaO/SiO 2 of 0.8 and various TiO 2 content was shown where the viscosity decreased with increasing temperatures.

AB - A study was conducted to investigate the Influence of TiO 3 on the Viscous behavior of calcium silicate melts containing 17 mass% Al 2O 3 and 10 mass% MgO. Samples were synthesized using reagent grade chemicals of CaO, SiO 2, MgO, Al 2O 3, and TiO 2. The samples were premelted at 1 773 K under 0.4 L/min of Ar in a Pt crucible to obtain a homogeneous slag sample. Post-experimental chemical composition using X-Ray Fluorescence (XRF) spectroscopy showed no apparent change. The viscosity of 120 g of slag placed in a Pt crucible was measured using a rotating spindle connected to a calibrated Brookfield digital rheometer. Effect of TiO 2 at constant temperature of 1 773 K at various CaO/SiO 2 ratio was provided. The temperature dependence of the viscosity at CaO/SiO 2 of 0.8 and various TiO 2 content was shown where the viscosity decreased with increasing temperatures.

UR - http://www.scopus.com/inward/record.url?scp=84862962259&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84862962259&partnerID=8YFLogxK

U2 - 10.2355/isijinternational.52.158

DO - 10.2355/isijinternational.52.158

M3 - Article

AN - SCOPUS:84862962259

VL - 52

SP - 158

EP - 160

JO - ISIJ International

JF - ISIJ International

SN - 0915-1559

IS - 1

ER -