The paper describes the mechanical behavior of fine recycled concrete aggregate (FRCA) concrete according to the mineral admixtures. Three types of the mineral admixtures, i.e., fly ash (FA), ground-granulated blast-furnace slag (GGBS), and silica fume (SF), are used and the replacement ratios of FRCA are 50% and 100%. The dosages of the admixtures of FA, GGBS, and SF are determined with the normal dosage (30%, 40%, and 5.0%, respectively) based on the ACI committee reports (No. 232, 233, and 234) and half-normal dosage. The mechanical performance is investigated with the compressive and splitting tensile strength, and elastic modulus. Additionally, the total porosity is measured in natural fine aggregate (NFA) and FRCA 100% replaced specimens by mercury intrusion porosimetry (MIP) for investigating the relationship with the compressive strength. Based on the experimental test results, the mineral admixtures improve the mechanical performance of FRCA concrete. The effective dosages of FA, GGBS, and SF for FRCA concrete are investigated according to the replacement ratio of the FRCA. In particular, FRCA 100% replaced concrete may be possible to be used for the structural concrete members with the specific dosage of the mineral admixtures. The prediction of the splitting tensile strength and the elastic modulus by the codes or previous formulas exhibits underestimated and overestimated results, respectively. The relationship between the total porosity and the compressive strength of the FRCA concrete should be modified with more experimental tests.
Bibliographical noteFunding Information:
Funding: This research was supported by the Basic Science Research Program through the National Research Foundation of Korea (NRF) funded by the Ministry of Science and ICT (NRF #2020R1A2C1013043), and by the Korea Institute of Energy Technology Evaluation and Planning (KETEP) funded by the Ministry of Trade, Industry and Energy (#20201510100010).
Acknowledgments: The authors would like to thank the Ministry of Science and ICT of Korea and the Ministry of Trade, Industry and Energy of Korea.
© 2020 by the authors.
All Science Journal Classification (ASJC) codes
- Materials Science(all)
- Condensed Matter Physics