Microstructure and crystal structure development in porous titania coatings prepared from anhydrous titanium ethoxide solutions

Young-Joo Kim, L. F. Francis

Research output: Contribution to journalArticle

18 Citations (Scopus)

Abstract

Porous titania coatings were prepared by spin coating anhydrous titanium ethoxide-ethanol solutions in a controlled humidity atmosphere. Ti ethoxide reacted with atmospheric moisture during deposition, to form amorphous particles (approximately 200 nm), a dense layer or a combination of the two, depending on the processing conditions. Relatively humid atmospheres, low concentrations of Ti ethoxide in the coating solution and slow spinning rates favoured particle formation. These particulate coatings were typically composed of agglomerated particle clusters. Agglomeration could be prevented by adding hydroxypropyl cellulose to alkoxide solution to act as a steric stabilizer for newly formed particles. During thermal treatment, the coatings crystallized into the anatase phase and then transformed into the rutile structure at higher temperatures. The anatase-rutile transformation in porous coatings occurred over a range of 850-1150°C and strongly depended on microstructural features. More porous coatings with larger particle clusters transformed to rutile at lower temperatures. Tensile stress in the coating caused by constrained shrinkage inhibited the phase transformation. The substrate constraint slowed the transformation rate in coatings relative to free powder. Stress relief through rupture of particle cluster connections allowed transformation to occur at lower temperatures.

Original languageEnglish
Pages (from-to)4423-4433
Number of pages11
JournalJournal of Materials Science
Volume33
Issue number17
DOIs
Publication statusPublished - 1998 Jan 1

Fingerprint

Titanium
Crystal structure
Coatings
Microstructure
Titanium dioxide
Stress relief
titanium dioxide
Spin coating
Tensile stress
Powders
Temperature
Cellulose
Atmospheric humidity
Ethanol
Moisture
Agglomeration
Phase transitions
Heat treatment
Substrates
Processing

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

@article{659df2b6814247bbb4ec599037558ca6,
title = "Microstructure and crystal structure development in porous titania coatings prepared from anhydrous titanium ethoxide solutions",
abstract = "Porous titania coatings were prepared by spin coating anhydrous titanium ethoxide-ethanol solutions in a controlled humidity atmosphere. Ti ethoxide reacted with atmospheric moisture during deposition, to form amorphous particles (approximately 200 nm), a dense layer or a combination of the two, depending on the processing conditions. Relatively humid atmospheres, low concentrations of Ti ethoxide in the coating solution and slow spinning rates favoured particle formation. These particulate coatings were typically composed of agglomerated particle clusters. Agglomeration could be prevented by adding hydroxypropyl cellulose to alkoxide solution to act as a steric stabilizer for newly formed particles. During thermal treatment, the coatings crystallized into the anatase phase and then transformed into the rutile structure at higher temperatures. The anatase-rutile transformation in porous coatings occurred over a range of 850-1150°C and strongly depended on microstructural features. More porous coatings with larger particle clusters transformed to rutile at lower temperatures. Tensile stress in the coating caused by constrained shrinkage inhibited the phase transformation. The substrate constraint slowed the transformation rate in coatings relative to free powder. Stress relief through rupture of particle cluster connections allowed transformation to occur at lower temperatures.",
author = "Young-Joo Kim and Francis, {L. F.}",
year = "1998",
month = "1",
day = "1",
doi = "10.1023/A:1004476930349",
language = "English",
volume = "33",
pages = "4423--4433",
journal = "Journal of Materials Science",
issn = "0022-2461",
publisher = "Springer Netherlands",
number = "17",

}

Microstructure and crystal structure development in porous titania coatings prepared from anhydrous titanium ethoxide solutions. / Kim, Young-Joo; Francis, L. F.

In: Journal of Materials Science, Vol. 33, No. 17, 01.01.1998, p. 4423-4433.

Research output: Contribution to journalArticle

TY - JOUR

T1 - Microstructure and crystal structure development in porous titania coatings prepared from anhydrous titanium ethoxide solutions

AU - Kim, Young-Joo

AU - Francis, L. F.

PY - 1998/1/1

Y1 - 1998/1/1

N2 - Porous titania coatings were prepared by spin coating anhydrous titanium ethoxide-ethanol solutions in a controlled humidity atmosphere. Ti ethoxide reacted with atmospheric moisture during deposition, to form amorphous particles (approximately 200 nm), a dense layer or a combination of the two, depending on the processing conditions. Relatively humid atmospheres, low concentrations of Ti ethoxide in the coating solution and slow spinning rates favoured particle formation. These particulate coatings were typically composed of agglomerated particle clusters. Agglomeration could be prevented by adding hydroxypropyl cellulose to alkoxide solution to act as a steric stabilizer for newly formed particles. During thermal treatment, the coatings crystallized into the anatase phase and then transformed into the rutile structure at higher temperatures. The anatase-rutile transformation in porous coatings occurred over a range of 850-1150°C and strongly depended on microstructural features. More porous coatings with larger particle clusters transformed to rutile at lower temperatures. Tensile stress in the coating caused by constrained shrinkage inhibited the phase transformation. The substrate constraint slowed the transformation rate in coatings relative to free powder. Stress relief through rupture of particle cluster connections allowed transformation to occur at lower temperatures.

AB - Porous titania coatings were prepared by spin coating anhydrous titanium ethoxide-ethanol solutions in a controlled humidity atmosphere. Ti ethoxide reacted with atmospheric moisture during deposition, to form amorphous particles (approximately 200 nm), a dense layer or a combination of the two, depending on the processing conditions. Relatively humid atmospheres, low concentrations of Ti ethoxide in the coating solution and slow spinning rates favoured particle formation. These particulate coatings were typically composed of agglomerated particle clusters. Agglomeration could be prevented by adding hydroxypropyl cellulose to alkoxide solution to act as a steric stabilizer for newly formed particles. During thermal treatment, the coatings crystallized into the anatase phase and then transformed into the rutile structure at higher temperatures. The anatase-rutile transformation in porous coatings occurred over a range of 850-1150°C and strongly depended on microstructural features. More porous coatings with larger particle clusters transformed to rutile at lower temperatures. Tensile stress in the coating caused by constrained shrinkage inhibited the phase transformation. The substrate constraint slowed the transformation rate in coatings relative to free powder. Stress relief through rupture of particle cluster connections allowed transformation to occur at lower temperatures.

UR - http://www.scopus.com/inward/record.url?scp=0032157432&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0032157432&partnerID=8YFLogxK

U2 - 10.1023/A:1004476930349

DO - 10.1023/A:1004476930349

M3 - Article

AN - SCOPUS:0032157432

VL - 33

SP - 4423

EP - 4433

JO - Journal of Materials Science

JF - Journal of Materials Science

SN - 0022-2461

IS - 17

ER -