Physical properties of resin-reinforced glass lonomer cement modified with micro and nano-hydroxyapatite

Jong Jin Lee, Yong Keun Lee, Byung Jai Choi, Jae Ho Lee, Hyung Jun Choi, Heung Kyu Son, Ji Won Hwang, Seong Oh Kim

Research output: Contribution to journalArticlepeer-review

36 Citations (Scopus)

Abstract

Hydroxyapatite is a biologically compatible material and a major component of dental enamel and bone tissue. Because of its biocompatibility and structural similarity to human teeth and the skeletal system, a number of dental studies have evaluated its application as a bone substitute or dental restorative material. This study was to evaluate the differences in bonding strength and resistance to demineralization between micro-hydroxyapatite and nano-hydroxyapatite added to self-cured resinreinforced/modified glass ionomer cement. RelyX was used as the base glass ionomer cement material and for the control group. 10% micro-hydroxyapatite added glass ionomer cement was named experimental group 1, and 10% nano-hydroxyapatite added glass ionomer cement was named experimental group 2. Physical tests for IS09917-1:2007 in each group was acceptable, except the setting time of nano-hydroxyapatite added glass ionomer cement, which exceeded maximum setting time. Bonding strength was greatest in nano-hydroxyapatite glass ionomer cement, and cohesive failure was common in all specimens. When fractured surface was observed under SEM, spherical particles were observed in experimental groups containing hydroxyapatite particles, and they were more prevalent in nano-HA added glass ionomer cement group than in microhydroxyapatite added group. Both experimental groups exhibited greater resistance to demineralization compared to the control group, and there was no significant difference between the experimental groups. Under SEM, nano-hydroxyapatite added glass ionomer cement exhibited increased resistance to demineralization compared to micro-hydroxyapatite added glass ionomer cement.

Original languageEnglish
Pages (from-to)5270-5276
Number of pages7
JournalJournal of Nanoscience and Nanotechnology
Volume10
Issue number8
DOIs
Publication statusPublished - 2010 Aug

All Science Journal Classification (ASJC) codes

  • Bioengineering
  • Chemistry(all)
  • Biomedical Engineering
  • Materials Science(all)
  • Condensed Matter Physics

Fingerprint

Dive into the research topics of 'Physical properties of resin-reinforced glass lonomer cement modified with micro and nano-hydroxyapatite'. Together they form a unique fingerprint.

Cite this