Synthesis of Zn2SnO4 anode material by using supercritical water in a batch reactor

Jae Wook Lee, Chang Ha Lee

Research output: Contribution to journalArticlepeer-review

26 Citations (Scopus)

Abstract

Zn2SnO4 anode powders were successfully synthesized using supercritical water (SCW) and metal salt solutions with 10 min reaction time. Effect of NaOH concentration, Zn to Sn ratio, and synthesis temperature were studied with a SCW batch reactor. X-ray diffraction (XRD), scanning electron microscopy (SEM), and charge/discharge cycling tests were employed to characterize the physical properties and electrochemical performance of the as-prepared samples. Alkaline solution concentration and synthesis temperature played a key role in the production of single-phase Zn2SnO 4 powders. At a solution concentration of 0.3 M NaOH and a molar ratio of Zn:Sn = 2:1 at 400 °C and 30 MPa, the average size range of the pure Zn2SnO4 powders was 0.5-1.0 μm, and the morphology was nearly uniform and cubic-like in shape. The initial specific discharge capacity of the Zn2SnO4 powders prepared at this condition was 1526 mAh/g at a current density of 0.75 mA/cm2 in 0.05-3.0 V, and their irreversible capacity loss was 433 mAh/g. The discharge capacities of the Zn2SnO4 powders decreased with cycling and remained at 856 mAh/g after 50 cycles, which was 56% of the initial capacity.

Original languageEnglish
Pages (from-to)252-258
Number of pages7
JournalJournal of Supercritical Fluids
Volume55
Issue number1
DOIs
Publication statusPublished - 2010 Nov

Bibliographical note

Funding Information:
This subject is supported by the Basic Research Project (GP 2009-015-02) of the Korea Institute of Geoscience and Mineral Resources (KIGAM) and 21C Frontier Project (CDRS:16-2008-00-012-00) from the Ministry of Education, Science and Technology of Korea .

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Condensed Matter Physics
  • Physical and Theoretical Chemistry

Fingerprint

Dive into the research topics of 'Synthesis of Zn<sub>2</sub>SnO<sub>4</sub> anode material by using supercritical water in a batch reactor'. Together they form a unique fingerprint.

Cite this