The electron beam deposition of titanium on polyetheretherketone (PEEK) and the resulting enhanced biological properties

Cheol Min Han, Eun Jung Lee, Hyoun Ee Kim, Young Hag Koh, Keung N. Kim, Yoon Ha, Sung Uk Kuh

Research output: Contribution to journalArticle

129 Citations (Scopus)

Abstract

The surface of polyetheretherketone (PEEK) was coated with a pure titanium (Ti) layer using an electron beam (e-beam) deposition method in order to enhance its biocompatibility and adhesion to bone tissue. The e-beam deposition method was a low-temperature coating process that formed a dense, uniform and well crystallized Ti layer without deteriorating the characteristics of the PEEK implant. The Ti coating layer strongly adhered to the substrate and remarkably enhanced its wettability. The Ti-coated samples were evaluated in terms of their in vitro cellular behaviors and in vivo osteointegration, and the results were compared to a pure PEEK substrate. The level of proliferation of the cells (MC3T3-E1) was measured using a methoxyphenyl tetrazolium salt (MTS) assay and more than doubled after the Ti coating. The differentiation level of cells was measured using the alkaline phosphatase (ALP) assay and also doubled. Furthermore, the in vivo animal tests showed that the Ti-coated PEEK implants had a much higher bone-in-contact (BIC) ratio than the pure PEEK implants. These in vitro and in vivo results suggested that the e-beam deposited Ti coating significantly improved the potential of PEEK for hard tissue applications.

Original languageEnglish
Pages (from-to)3465-3470
Number of pages6
JournalBiomaterials
Volume31
Issue number13
DOIs
Publication statusPublished - 2010 May 1

    Fingerprint

All Science Journal Classification (ASJC) codes

  • Bioengineering
  • Ceramics and Composites
  • Biophysics
  • Biomaterials
  • Mechanics of Materials

Cite this